Saline soluble inorganic fibres

ABSTRACT

Refractory fibres are disclosed for which a vacuum cast preform of the fibre has a shrinkage of 3.5% or less when exposed to 1260° C. for 24 hours. The fibres comprise CaO, SiO 2 , SrO, and optionally ZrO 2  any incidental impurities amounting to less than 2 mol % in total. To achieve the shrinkage performance stated the SiO 2  excess (defined as the amount of SiO 2  calculated as remaining after the above named constituents are crystallised as silicates) exceeds 26 mol %. Preferred fibres comprise:--CaO less than 33.8 mol %, SiO 2  more than 62.1 mol %, and more preferably comprise:--CaO 12.9 to 31.9 mol %, SrO 2.6 to 15.5 mol %, SiO 2  63.2 to 71.3 mol %, ZrO 2  0 to 5.4 mol %.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to saline soluble, non-metallic, amorphous, inorganic oxide, refractory fibrous materials. The invention particularly relates to glassy fibres having silica as their principal constituent.

2. Description of the Related Art

Inorganic fibrous materials are well known and widely used for many purposes. (e.g. as thermal or acoustic insulation in bulk, mat, or blanket form, as vacuum formed shapes, as vacuum formed boards and papers, and as ropes, yarns or textiles; as a reinforcing fibre for building materials; as a constituent of brake blocks for vehicles). In most of these applications the properties for which inorganic fibrous materials are used require resistance to heat, and often resistance to aggressive chemical environments.

Inorganic fibrous materials can be either glassy or crystalline. Asbestos is an inorganic fibrous material one form of which has been strongly implicated in respiratory disease.

It is still not clear what the causative mechanism is that relates some asbestos with disease but some researchers believe that the mechanism is mechanical and size related. Asbestos of a critical size can pierce cells in the body and so, through long and repeated cell injury, have a bad effect on health. Whether this mechanism is true or not regulatory agencies have indicated a desire to categorise any inorganic fibre product that has a respiratory fraction as hazardous, regardless of whether there is any evidence to support such categorisation. Unfortunately for many of the applications for which inorganic fibres are used, there are no realistic substitutes.

Accordingly there is a demand for inorganic fibres that will pose as little risk as possible (if any) and for which there are objective grounds to believe them safe.

A line of study has proposed that if inorganic fibres were made that were sufficiently soluble in physiological fluids that their residence time in the human body was short; then damage would not occur or at least be minimised. As the risk of asbestos linked disease appears to depend very much on the length of exposure this idea appears reasonable. Asbestos is extremely insoluble.

As intercellular fluid is saline in nature the importance of fibre solubility in saline solution has long been recognised. If fibres are soluble in physiological saline solution then, provided the dissolved components are not toxic, the fibres should be safer than fibres which are not so soluble. The shorter the time a fibre is resident in the body the less damage it can do. H. Forster in `The behaviour of mineral fibres in physiological solutions` (Proceedings of 1982 WHO IARC Conference, Copenhagen, Volume 2, pages 27-55(1988)) discussed the behaviour of commercially produced mineral fibres in physiological saline solutions. Fibres of widely varying solubility were discussed.

International Patent Application No. WO87/05007 disclosed that fibres comprising magnesia, silica, calcia and less than 10 wt % alumina are soluble in saline solution. The solubilities of the fibres disclosed were in terms of parts per million of silicon (extracted from the silica containing material of the fibre) present in a saline solution after 5 hours of exposure. The highest value revealed in the examples had a silicon level of 67 ppm. In contrast, and adjusted to the same regime of measurement, the highest level disclosed in the Forster paper was equivalent to approximately 1 ppm. Conversely if the highest value revealed in the International Patent Application was converted to the same measurement regime as the Forster paper it would have an extraction rate of 901,500 mg Si/kg fibre--i.e. some 69 times higher than any of the fibres Forster tested, and the fibres that had the highest extraction rate in the Forster test were glass fibres which had high alkali contents and so would have a low melting point. This is convincingly better performance even taking into account factors such as differences in test solutions and duration of experiment.

International Patent Application No. WO89/12032 disclosed additional fibres soluble in saline solution and discusses some of the constituents that may be present in such fibres. Among such constituents are ZrO₂ and this document claims (among other things) processes using fibres of composition (in weight %):--ZrO₂ 0.06-10%; SiO₂ 35-70%; MgO 0-50%; CaO 0-64.5%. However the patent actually discloses a much more limited range of zirconia containing materials.

European Patent Application No. 0399320 disclosed glass fibres having a high physiological solubility.

Further patent specifications disclosing selection of fibres for their saline solubility include for example European 0412878 and 0459897, French 2662687 and 2662688, PCT WO86/04807, WO90/02713, WO92/09536, and WO93/22251, and U.S. Pat. No. 5,250,488.

The refractoriness of the fibres disclosed in these various prior art documents varies considerably. The maximum service temperature of any of the above mentioned fibres (when used as refractory insulation) is up to 815° C. (1500° F.).

Among saline soluble commercial fibres usable at temperatures higher than 815° C. are SUPERWOOL™ a fibre manufactured by The Morgan Crucible Company plc and which has a maximum use temperature of 1050° C. and a composition of SiO₂ 65 wt %; CaO 29 wt %; MgO 5 wt %; Al₂ O₃ 1 wt %. A similar fibre is INSULFRAX™ a fibre made by Carborundum Company which has a continuous use limit of 1000° C. (1832° F.) and which melts at 1260° C. (2300° F.). This has a composition of SiO₂ 65 wt %; CaO 31.1 wt %; MgO 3.2 wt %; Al₂ O₃ 0.3 wt % and Fe₂ O₃ 0.3 wt %.

The applicant's earlier International Patent Application WO93/15028 disclosed saline soluble fibres comprising CaO, MgO and SiO₂ and optionally ZrO₂ usable at temperatures in excess of 1000° C. but gave no indication that fibres could be used at still higher temperatures. That same application also discloses methods of predicting the saline solubility of glasses and for screening for the refractoriness of glasses, although whether such glasses can form fibres is a complex function of many characteristics, e.g. viscosity.

In discussing the above mentioned predictive methods International Patent Application WO93/15028 mentions some compositions containing strontium oxide as a constituent but fibres of these compositions were not made.

The applicants have realised that failure of fibres at high temperature occurs primarily upon devitrification of the fibre; if on devitrification insufficient silica is left the fibres will fail through having a shrinkage of greater than 3.5%. Accordingly the applicants have looked to what materials are formed on devitrification and in their earlier International Patent Application No. PCT/GB94/00053 they disclose refractory fibres comprising CaO, SiO₂, MgO, optionally ZrO₂, optionally less than 0.75 mol % Al₂ O₃ and in which the SiO₂ excess (defined as the amount of SiO₂ calculated as remaining after the above named constituents are crystallised as silicates) exceeds 21.8 mol %.

The physical basis for the importance of SiO₂ excess may be that it indicates how much silica is left to maintain a glassy phase on crystallisation of the other constituents as silicate materials. Further, the silicate materials that form on devitrification may become liquid or flow at 1260° C. so causing shrinkage.

SUMMARY OF THE INVENTION

The applicants have found that some systems comprising strontium oxide calcium oxide and silica may form fibres usable at temperatures of up to 1260° C. whereas other strontium containing systems do not form such usable fibres. In particular the applicants have found that partial replacement of SrO for MgO in the CaO/MgO/(ZrO₂)/SiO₂ fibres of their earlier application PCT/GB94/00053 does not result in success whereas substitution of SrO for MgO tends to give usable fibres.

Accordingly the present invention provides a refractory fibre for which a vacuum cast preform of the fibre has a shrinkage of 3.5% or less when exposed to 1260° C. for 24 hours and comprising CaO, SiO₂, SrO, and optionally ZrO₂ any incidental impurities amounting to less than 2 mol % in total, and in which the SiO₂ excess (defined as the amount of SiO₂ calculated as remaining after the above named constituents are crystallised as silicates) exceeds 26 mol %.

The quantity of potentially fluxing constituents such as alkali metals and other incidental impurities (e.g. iron oxides) should be kept low.

DETAILED DESCRIPTION OF SPECIFIC EMBODIMENTS

From the compositions tested it appears that preferably the fibre comprises:

    ______________________________________                                         CaO              less than 33.8 mol %                                          SiO.sub.2        more than 62.1 mol %.                                         ______________________________________                                    

and more preferably comprises:

    ______________________________________                                         CaO               12.9 to 31.9 mol %                                           SrO               2.6 to 15.5 mol %                                            SiO.sub.2         63.2 to 71.3 mol %                                           ZrO.sub.2         0 to 5.4 mol %.                                              ______________________________________                                    

The applicants have investigated, for their saline solubility and refractoriness, a range of fibre compositions. These fibres were formed by blowing the molten constituents from a melt stream in a conventional manner but the invention is not limited to blown fibres and also encompasses fibres formed by spinning or any other means.

Tables 1 & 2 show the results of these tests. Table 1 is divided into the CaO-SrO-ZrO₂ -SiO₂ system, the CaO-SrO-SiO₂ system, and some comparative examples (which were never made as fibres). Table 1 indicates for each fibre the linear shrinkages at 800°, 1000°, 1200°, and 1260° C. (not all samples measured at every temperature); mole percent composition (based on the constituents CaO, MgO, SrO, ZrO₂, Al₂ O₃, TiO₂ and SiO₂); crystalline constituents formed on devitrification (see below); SiO₂ excess (calculation for this figure shown below) and, for the CaO-SrO-SiO₂ fibres and comparative examples, the calculated CaSiO₃ to SrSiO₃ ratio. Each sample that has a satisfactory shrinkage of 3.5% or less at 1260° C. is indicated by a composition shown in bold. Those compositions that fail to meet the shrinkage criterion are indicated in plain text.

Table 2 shows for the CaO-SrO-ZrO₂ -SiO₂ system and the CaO-SrO-SiO₂ system the solubilities (as parts per million) of selected constituents of the fibres in saline solution measured by the method described below and shows the total of the named solubilities. This table is ordered in the same manner as Table 1 for convenient comparison.

3 strontium containing systems were investigated. These are:

CaO-MgO-SrO-SiO₂

CaO-SrO-SiO₂

CaO-SrO-ZrO₂ -SiO₂

In the CaO-MgO-SrO-SiO₂ system very poor results were found--MgO and SrO evidently being incompatible--and so the present invention treats MgO as an incidental impurity that must be held within the 2 mol % total given above. The applicants have good reason to believe that the maximum level for MgO may be as low as 1% and preferably the MgO content is kept as low as possible. To some extent therefore SrO may be treated as being in substitution of MgO in the fibres of PCT/GB94/00053.

The CaO-SrO-SiO₂ and CaO-SrO-ZrO₂ -SiO₂ systems are discussed separately below.

(1) CaO-SrO-SiO₂

This is a simple system in that only CaSiO₃, SrSiO₃ and SiO₂ crystallise. Therefore all the CaO forms as CaSiO₃ and all the SrO forms as SrSiO₃. The resulting excess SiO₂ can then be calculated. However CaSiO₃ and SrSiO₃ form a complete solid solution between them, with the melting point being 1580° C. for SrSiO₃ and 1540° C. for CaSiO₃, and with a minimum in melting point lying between these extremes. It is reasonable to expect that compositions having significant quantities of both CaSiO₃ and SrSiO₃ will have lower melting points than either those containing high CaSiO₃ and low SrSiO₃, or those containing high SrSiO₃ and low CaSiO₃ contents. Table 1 shows that for those fibres with a CaSiO₃ /SrSiO₃ ratio of greater than 2 (those fibres lying below line "A") a silica excess of greater than 26 mol % neatly divides the workable fibres (having preform shrinkages of less than 3.5% and shown in bold) from those that are not. For those fibres above line "A" where the CaSiO₃ /SrSiO₃ ratio is less than 2 a silica excess of 34 mol % is required to divide the workable from the unworkable compositions. However the applicants suspect that there will be a lower limit (perhaps around CaSiO₃ /SrSiO₃ ratio 0.5) below which a lower silica excess will prevail again.

(2) CaO-SrO-ZrO₂ -SiO₂

This is a more complicated system than the CaO-SrO-SiO₂ system, with at least 5 components crystallising out. These are 2CaO.ZrO₂.4SiO₂, 6SrO.ZrO₂.5SiO₂, CaSiO₃, SrSiO₃ and SiO₂.

For those compositions studied all the ZrO₂ crystallises as 2CaO.ZrO₂.4SiO₂ and 6SrO.ZrO₂.5SiO₂ (if more ZrO₂ is present ZrO₂.SiO₂ will crystallise also). To fit the relative amounts of phases indicated by X-ray analysis the assumption has been made that the thermodynamics of formation of the 2CaO.ZrO₂.4SiO₂ and 6SrO.ZrO₂.5SiO₂ phases are very similar and that the distribution of ZrO₂ between these phases can be dealt with statistically. The relative ratios of these phases is then determined by the ratios of the CaO and SrO of the initial composition. The issue is further complicated by the fact that in these phases there are 2CaO's per ZrO₂ and 6SrO's per ZrO₂ respectively i.e. 3 times more SrO to CaO is required to form equal amounts of 2CaO.ZrO₂.4SiO₂ and 6SrO.ZrO₂.5SiO₂. Therefore to calculate how the ZrO₂ is split between 2CaO.ZrO₂.4SiO₂ and 6SrO.ZrO₂.5SiO₂ the applicants calculate the ratio of CaO/SrO and multiply by 3, because the CaO is 3 times more likely to form 2CaO.ZrO₂.4SiO₂ than SrO is to form 6SrO.ZrO₂.5SiO₂. The ZrO₂ content is divided by this figure to give the amount of 6SrO.ZrO₂.5SiO₂ produced. The remaining ZrO₂ forms 2CaO.ZrO₂.4SiO₂. (Of course if there is sufficient ZrO₂ to exhaust either the CaO or SrO the calculation must be modified accordingly). Now any remaining CaO forms CaSiO₃ and any remaining SrO forms SrSiO₃. The remaining excess SiO₂ can then be calculated.

With all these SrO containing compositions there will be inevitable discrepancies around the boundary areas. Small changes in the composition of only 0.1-0.2% are usually sufficient to be the difference between failure and pass at the boundary. In these systems there are considerable difficulties in analysing for SrO, CaO and SiO₂ together by X-ray fluorescence (XRF) because their XRF spectra interfere with each other thereby making it difficult to construct an accurate quantitative XRF programme for these systems. This means the accuracy of the reported compositions is less than would be expected for general XRF samples.

These factors may explain why two compositions (F29 and F16) in the CaO-SrO-ZrO₂ -SiO₂ system show as failures when their excess SiO₂ figure would indicate them as being potentially useful fibres.

Under the heading "Comparative compositions" in Table 1 are shown two types of material. Those with the prefix "SCS" are compositions mentioned in WO/93/15028 as being potential refractory glass forming compositions. None of these fibres were made and as will be seen from the figures for excess SiO₂ given would not fall within the scope of the present application. The compositions shown with the prefix "BS" are fibres made containing appreciable amounts of both MgO and SrO and as can be seen these materials have an unsatisfactory shrinkage. Silica excesses have not been calculated for these compositions.

The applicants have looked to the various incidental impurities that can occur in inorganic oxide refractory fibres (e.g. alkali oxides and iron oxide) and have found that the impurity levels that can be tolerated vary according to the proportions of the main constituents of the fibre. Fibres containing high levels of ZrO₂ for example can tolerate higher levels of Na₂ O or Fe₂ O₃ than fibres with low levels of ZrO₂. Accordingly the applicants propose a maximum level of incidental impurities of 2 mol %, the maximum level that will be tolerable will however vary as mentioned above.

The following describes in detail the methods used to measure shrinkage and solubility.

Shrinkage was measured by proposed ISO standard ISO/TC33/SC2/N220 (equivalent to British Standard BS 1920, part 6,1986) with some modifications to account for small sample size. The method in summary comprises the manufacture of vacuum cast preforms, using 75 g of fibre in 500 cm³ of 0.2% starch solution, into a 120×65 mm tool. Platinum pins (approximately 0.1-0.3 mm diameter) were placed 100×45 mm apart in the 4 corners. The longest lengths (L1 & L2) and the diagonals (L3 & L4) were measured to an accuracy of ±5 μm using a travelling microscope. The samples were placed in a furnace and ramped to a temperature 50° C. below the test temperature at 400° C./hour and ramped at 120° C./hour for the last 50° C. to test temperature and left for 24 hours. The shrinkage values are given as an average of the 4 measurements.

It should be noted that although this is a standard way of measuring shrinkage of fibre it has an inherent variability in that the finished density of the preform may vary depending on casting conditions. Further it should be noted that fibre blanket will usually have a higher shrinkage than a preform made of the same fibre. Accordingly the 3.5% figure mentioned in this specification is likely to translate as a higher shrinkage in finished blanket.

Solubility was measured by the following method.

The fibre was first chopped--2.5 g of fibre (deshotted by hand) was liquidised with 250 cm³ of distilled water in a domestic Moulinex (Trade Mark) food blender for 20 seconds. The suspension was then transferred to a 500 cm³ plastic beaker and allowed to settle after which as much liquid as possible was decanted and the remaining liquid removed by drying in an oven at 110° C.

The solubility test apparatus comprised a shaking incubator water bath, and the test solution had the following composition:

    ______________________________________                                         Compound        Name         Grams                                             ______________________________________                                         NaCl            Sodium chloride                                                                             6.780                                             NH.sub.4 Cl     Ammonium chloride                                                                           0.540                                             NaHCO.sub.3     Sodium bicarbonate                                                                          2.270                                             Na.sub.2 HPO.sub.4.H.sub.2 O                                                                   Disodium hydrogen                                                                           0.170                                                             phosphate                                                      Na.sub.3 C.sub.6 H.sub.5 O.sub.7.2H.sub.2 O                                                    Sodium citrate                                                                              0.060                                                             dihydrate                                                      H.sub.2 NCH.sub.2 CO.sub.2 H                                                                   Glycine      0.450                                             H.sub.2 SO.sub.4 s.g. 1.84                                                                     Sulphuric acid                                                                              0.050                                             ______________________________________                                    

The above materials were diluted to 1 liter with distilled water to form a physiological-like saline solution.

0.500 grams ±0.0003 grams of chopped fibre was weighed into a plastic centrifuge tube and 25 cm³ of the above saline solution added. The fibre and saline solution was shaken well and inserted into the shaking incubator water bath maintained at body temperature (37° C.±1° C.). The shaker speed was set at 20 cycles/minute.

After the desired period (usually 5 hours or 24 hours) the centrifuge tube was removed and centrifuged at 4500 revs/minute for approximately 5 minutes. Supernatant liquid was then drawn off using a syringe and hypodermic needle. The needle was then removed from the syringe, air expelled from the syringe, and the liquid passed through a filter (0.45 micron cellulose nitrate membrane filter paper WCN type from Whatman Labsales Limited!) into a clean plastic bottle. The liquid was then analysed by atomic absorption using a Thermo Jarrell Ash Smith - Hiefje II machine.

The operating conditions were as follows using a nitrous oxide and acetylene flame:

    ______________________________________                                                 WAVELENGTH   BAND    CURRENT                                           ELEMENT (nm)         WIDTH   (mA)     FLAME                                    ______________________________________                                         Al      309.3        1.0     8        Fuel Rich                                SiO.sub.2                                                                              251.6        0.3     12       Fuel Rich                                CaO     422.7        1.0     7        Fuel Lean                                MgO     285.2        1.0     3        Fuel Lean                                SrO     460.7        0       12       Fuel Lean                                ______________________________________                                    

The procedure and standards adopted for determining the above elements were as set out below.

SiO₂ can be determined without dilution up to 250 ppm concentration (1 ppm 1 mg/Liter). Above this concentration an appropriate dilution was made volumetrically. A 0.1% KCl solution (0.1 g in 100 cm³) was added to the final dilution to prevent ionic interference. NB If glass apparatus is used, prompt analysis is necessary.

From a stock solution of 1000 ppm pure ignited silica (99.999%) (fused with Na₂ CO₃ at 1200° C. for 20 minutes in a platinum crucible (0.2500 g SiO₂ /2 g Na₂ CO₃) and dissolved in dilute hydrochloric acid (4 molar) made up to 250 cm³ with distilled water in a plastic volumetric flask) the following standards were produced:

    ______________________________________                                         STANDARD (ppm SiO.sub.2)                                                                       STOCK SOLUTION (cm.sup.3)                                      ______________________________________                                         10.0            1.0                                                            20.0            2.0                                                            30.0            3.0                                                            50.0            5.0                                                            100.0           10.0                                                           250.0           25.0                                                           ______________________________________                                    

Add 0.1% KCl to each standard before making to 100 cm³.

Aluminium may be measured directly from the sample without dilution. Standards of 1.0, 5.0 and 10.0 ppm Al may be used. For calibration readings are multiplied by 1.8895 to convert from Al to Al₂ O₃.

A standard Al atomic absorption solution (e.g. BDH 1000 ppm Al) was bought and diluted using an accurate pipette to the desired concentration. 0.1% KCl was added to prevent ionic interference.

Calcium may require dilutions on the sample before determination can be carried out (i.e. ×10 and ×20 dilutions). Dilutions must contain 0.1% KCl.

A standard Ca atomic absorption solution (e.g. BDH 1000 ppm Ca) was diluted with distilled water and an accurate pipette to give standards of 0.5, 4.0 and 10.0 ppm. 0.1% KCl is added to prevent ionic interference. To convert readings obtained from Ca to CaO a factor of 1.4 was used.

Strontium is measured against a standard atomic absorption solution (Aldrich 970 μm/ml). Three standards are prepared to which 0.1% KCl is added (Sr ppm! 9.7,3.9 & 1.9). Dilutions of ×10 and ×20 are nromally made to measure Sr level in the sample. SrO is then calculated as 1.183×Sr.

Magnesium may require dilutions on the sample before determinations can be made (i.e. ×10 and ×20). Add 0.1% KCl to each dilution. To convert Mg to MgO multiply by 1.658.

A standard Mg atomic absorption solution (e.g. BDH 1000 ppm Mg) was diluted with distilled water and an accurate pipette to give standards of 0.5, 1.0 and 10.0 ppm Mg. 0.1% KCl was added to prevent ionic interference.

All stock solutions were stored in plastic bottles.

The above has discussed resistance to shrinkage of preforms exposed to 1260° C. for 24 hours. This is an indication of the maximum use temperature of a fibre. In practice fibres are quoted for a maximum continuous use temperature and a higher maximum exposure temperature. It is usual in industry when selecting a fibre for use at a given temperature to choose a fibre having a higher continuous use temperature than that nominally required for the intended use. This is so that any accidental increase in temperature does not damage the fibres. It is quite usual for a margin of 100° to 150° C. to be given. Accordingly this invention extends to use of the claimed fibres at elevated temperatures (i.e. at temperatures where the refractoriness of fibres is important) and not just to use at 1260° C.

It will be evident that incidental impurity levels are preferably kept as low as possible. The applicants surmise that as the various crystalline materials crystallise from the fibres impurities migrate to the grain boundaries and concentrate there. Thus a small impurity can have a very large effect.

                                      TABLE 1                                      __________________________________________________________________________     CaO--SrO--ZrO2--SiO2 System                                                    __________________________________________________________________________         Shrinkage          Composition                                                                            mol %                                           Comp.                                                                              800° C.                                                                     1000° C.                                                                     1200° C.                                                                     1260° C.                                                                     CaO                                                                               MgO                                                                               SrO                                                                               ZrO2                                                                              Al2O3                                                                              TiO2                                                                              SiO2                                 __________________________________________________________________________     F33 1.30                                                                               8.20           30.2                                                                              0.9                                                                               2.6                                                                               5  0.2 0.1                                                                               60.9                                 F28 1.50                                                                               5.10           31.6                                                                              0.9                                                                               2.6                                                                               2.4                                                                               0.3 0.1                                                                               62.1                                 F15 0.40                                                                               7.70           27.7                                                                              0.9                                                                               2.8                                                                               5  0.1 0.1                                                                               63.4                                 F34 0.10                                                                               6.00           24.9                                                                              0.8                                                                               5.7                                                                               4.8                                                                               0.2 0.1                                                                               63.8                                 F20     1.40 1.90 2.50 25.8                                                                              0.8                                                                               2.7                                                                               5.4                                                                               0.1 0.1                                                                               65.2                                 F1  1.10                                                                               1.50      2.30 29.4                                                                              0.9                                                                               2.7                                                                               2.5                                                                               0.1 0.1                                                                               64.3                                 F29     2.60      5.80 28.8                                                                              0.8                                                                               5.5                                                                               2.5                                                                               0.2    64.4                                 F16 0.40                                                                               4.20 6.10      22.7                                                                              0.8                                                                               5.7                                                                               5.2                                                                               0.1 0.1                                                                               65.4                                 F6  0.50                                                                               0.70 1.60 1.80 27.3                                                                              0.8                                                                               2.6                                                                               2.5                                                                               0.1 0.1                                                                               66.6                                 F2  0.80                                                                               1.10      2.80 24.3                                                                              0.8                                                                               5.7                                                                               2.5                                                                               0.1 0.1                                                                               66.7                                 F24     0.50 1.10 1.50 23.2                                                                              0.8                                                                               2.7                                                                               5.2                                                                               0.1 0.1                                                                               68                                   F21     0.60 1.60 2.70 20.2                                                                              0.8                                                                               5.7                                                                               5.4                                                                               0.1 0.1                                                                               67.7                                 F11 -0.10                                                                              0.30 0.90 1.40 25.3                                                                              0.8                                                                               2.4                                                                               2.4                                                                               0.1 0.1                                                                               68.4                                 F7  0.30                                                                               0.70 1.30 1.90 22.3                                                                              0.6                                                                               5.6                                                                               2.6                                                                               0.1 0.1                                                                               68.8                                 F3  0.30                                                                               0.70      2.50 18.8                                                                              0.5                                                                               8.8                                                                               2.7                                                                               0.1 0.1                                                                               69                                   F25     0.40 0.90 1.10 17.7                                                                              0.7                                                                               5.8                                                                               5.3                                                                               0.1 0.1                                                                               70.6                                 F12 -0.20                                                                              0.50 0.60 1.00 19.6                                                                              0.8                                                                               5.8                                                                               2.6                                                                               0.1 0.1                                                                               71.3                                 __________________________________________________________________________                                               Excess                               Comp.                                                                              SrO.ZrO2.2SiO2                                                                          2CaO.ZrO2.4SiO2                                                                          6SrO.ZrO2.5SiO2                                                                         CaSiO3                                                                              SrZiO3                                                                              SiO2                                 __________________________________________________________________________     F33 None     4.86      0.14     20.49                                                                               1.74 18.53                                F28 None     2.33      0.07     28.93                                                                               2.21 23.30                                F15 None     4.83      0.17     18.04                                                                               1.19 23.41                                F34 None     4.43      0.37     18.03                                                                               3.50 24.50                                F20 None     5.21      0.19     15.38                                                                               1.57 28.47                                F1  None     2.42      0.08     24.55                                                                               2.24 27.43                                F29 None     2.33      0.17     21.94                                                                               4.47 27.82                                F16 None     4.76      0.44     13.17                                                                               3.09 21.91                                F6  None     2.42      0.08     22.46                                                                               2.12 31.94                                F2  None     2.30      0.20     19.89                                                                               4.53 32.29                                F24 None     5.00      0.20     13.20                                                                               1.49 32.31                                F21 None     4.99      0.51     10.42                                                                               2.85 32.52                                F11 None     2.31      0.09     20.68                                                                               2.35 35.68                                F7  None     2.39      0.22     17.54                                                                               4.29 38.35                                F3  None     2.29      0.42     14.24                                                                               8.27 37.28                                F25 None     4.74      0.56     9.22 2.25 38.38                                F12 None     2.35      0.25     14.90                                                                               4.11 41.64                                __________________________________________________________________________     CaO--SrO--SiO2 System                                                          __________________________________________________________________________     Shrinkage              Composition                                                                             mol %                                          Comp.                                                                              800° C.                                                                     1000° C.                                                                     1200° C.                                                                     1260° C.                                                                     CaO                                                                               MgO                                                                               SrO                                                                               ZrO2                                                                              Al2O3                                                                              TiO2                                                                              SiO2                                 __________________________________________________________________________     E29 2.20                                                                               3.90      5.70 23.3                                                                              0.6                                                                               11.8  0.2    64                                   E30 1.20                                                                               2.60 4.00 4.70 17.8                                                                              0.5                                                                               15.2                                                                              0.1                                                                               0.2 0.1                                                                               68.2                                 E19 0.90                                                                               1.20 1.90 1.70 20 0.6                                                                               12 0.1                                                                               0.3    66.9                                 E4  0.40                                                                               1.40      0.60 19 0.5                                                                               11.5                                                                              0.2                                                                               0.1 0.1                                                                               68.7                                 E20 0.30                                                                               1.00 1.10 1.20 14.8                                                                              0.7                                                                               15.5                                                                              0.1                                                                               0.3    68.6                                 E5  0.30                                                                               0.40      0.50 12.9                                                                              0.3                                                                               15.5                                                                              0.1                                                                               0.1 0.1                                                                               71                                   E26 1.50                                                                               1.20      4.90 38.2                                                                              1  2.6   0.2    57.9                                 E27 1.30                                                                               2.00 4.90 7.90 33.8                                                                              0.9                                                                               5.6   0.2    59.5                                 E16 1.10                                                                               1.70 5.10 3.50 36.2                                                                              0.9                                                                               2.6   0.2 0.1                                                                               60                                   E28 2.80                                                                               5.70      7.90 28.6                                                                              0.9                                                                               8.2   0.2    62.1                                 E17 0.90                                                                               1.00 2.30 2.90 30.1                                                                              0.8                                                                               5.7   0.3    63.2                                 E6  0.50                                                                               0.70      0.20 32 0.9                                                                               2.6   0.2    64.2                                 E1  0.90                                                                               1.00      1.70 31.9                                                                              0.8                                                                               2.6   0.2 0.1                                                                               64.4                                 E18 0.70                                                                               1.40 1.30 1.40 25.3                                                                              0.6                                                                               8.8                                                                               0.1                                                                               0.3    65                                   E2      1.00      2.50 27.4                                                                              0.8                                                                               5.4                                                                               0.1                                                                               0.2 0.1                                                                               66.1                                 E7      0.60      0.80 26.9                                                                              0.6                                                                               5.7   0 2 0.1                                                                               66.5                                 E11 0.20                                                                               0.70 1.30 0.80 29.7                                                                              0.7                                                                               2.6   0.2 0.1                                                                               66.6                                 E3  0.50                                                                               1.00 1.50 1.50 22.4                                                                              0.6                                                                               8.3                                                                               0.1                                                                               0.1 0.1                                                                               68.4                                 E12 0.20                                                                               0.60      0.90 23.5                                                                              0.6                                                                               5.7                                                                               0.2                                                                               0.4    69.7                                 __________________________________________________________________________                                              CaSiO3/                                                                    Excess                                                                             SrSiO3                                Comp.                                                                              SrO.ZrO2.2SiO2                                                                         2CaO.ZrO2.4SiO2                                                                         6SrO.ZrO2.5SiO2                                                                        CaSiO3                                                                             SrZiO3                                                                             SiO2                                                                               ratio                                 __________________________________________________________________________     E29 None    None     None    23.33                                                                              11.81                                                                              28.86                                                                              1.98                                  E30 None    None     None    17.77                                                                              15.17                                                                              33.26                                                                              1.17                                  E19 None    None     None    20.04                                                                              12.05                                                                              34.91                                                                              1.66                                  E4  None    None     None    19.99                                                                              11.47                                                                              39.25                                                                              1.65                                  E20 None    None     None    14.78                                                                              15.49                                                                              39.35                                                                              0.95                                  E5  None    None     None    12.93                                                                              15.47                                                                              42.61                                                                              0.84                                  E26 None    None     None    38.25                                                                              2.64                                                                               17.02                                                                              14.50                                 E27 None    None     None    33.76                                                                              5.57                                                                               20.17                                                                              8.06                                  E16 None    None     None    36.22                                                                              2.64                                                                               21.14                                                                              13.74                                 E28 None    None     None    28.57                                                                              8.19                                                                               25.34                                                                              3.49                                  E17 None    None     None    30.11                                                                              5.65                                                                               27.44                                                                              5.33                                  E6  None    None     None    32.01                                                                              2.65                                                                               29.54                                                                              12.09                                 E1  None    None     None    31.95                                                                              2.85                                                                               29.90                                                                              12.03                                 E18 None    None     None    25.29                                                                              8.77                                                                               30.95                                                                              2.88                                  E2  None    None     None    27.41                                                                              5.41                                                                               33.29                                                                              5.07                                  E7  None    None     None    26.94                                                                              5.87                                                                               33.99                                                                              4.75                                  E11 None    None     None    29.70                                                                              2.84                                                                               34.28                                                                              11.25                                 E3  None    None     None    22.37                                                                              8.34                                                                               37.99                                                                              2.68                                  E12 None    None     None    23.55                                                                              5.85                                                                               40.50                                                                              4.17                                  __________________________________________________________________________     Comparative compositions                                                       __________________________________________________________________________     Shrinkage              Composition                                                                             mol %                                          Comp.                                                                              800° C.                                                                     1000° C.                                                                     1200° C.                                                                     1260° C.                                                                     CaO                                                                               MgO                                                                               SrO                                                                               ZrO2                                                                              Al2O3                                                                              TiO2                                                                              SiO2                                 __________________________________________________________________________     SCS(A)                 22.4  25.7         51.9                                 SCS(C)                 35    12.6         52.4                                 SCS(B)                 11.1  38.1         50.8                                 BS-2                                                                               0.60                                                                               1.30      7.50 9.6                                                                               18.2                                                                              5.3                                                                               0.1                                                                               0.1 0.1                                                                               66.6                                 BS-1    1.30      3.90 14.4                                                                              17.8                                                                              2.3                                                                               0.3                                                                               0.2 0.1                                                                               64.8                                 BS-4                                                                               0.40                                                                               1.30      12.50                                                                               9.8                                                                               14.8                                                                              5.4                                                                               2.9                                                                               0.1 0.1                                                                               67                                   BS-3                                                                               0.20                                                                               1.20      4.50 14 14.4                                                                              2.5                                                                               2.8                                                                               0.1 0.1                                                                               68.2                                 BS-5                                                                               0.50                                                                               1.20      12.90                                                                               14.3                                                                              13.3                                                                              5.2                                                                               0.3                                                                               0.1 0.1                                                                               68.7                                 BS-6    1.10      23.00                                                                               13.2                                                                              11.9                                                                              5.2                                                                               2.7                                                                               0.1 0.1                                                                               66.8                                 __________________________________________________________________________                                              CaSiO3/                                                                    Excess                                                                             SrSiO3                                Comp.                                                                              SrO.ZrO2.2SiO2                                                                         2CaO.ZrO2.4SiO2                                                                         6SrO.ZrO2.5SiO2                                                                        CaSiO3                                                                             SrZiO3                                                                             SiO2                                                                               ratio                                 __________________________________________________________________________     SCS(A)                                                                             None    None     None    29.70                                                                              2.64                                                                               19.56                                                                              11.25                                 SCS(C)                                                                             None    None     None    22.37                                                                              8.34                                                                               21.69                                                                              2.68                                  SCS(B)                                                                             None    None     None    23.55                                                                              5.65                                                                               21.60                                                                              4.17                                  BS-2                                                                           BS-1                                                                           BS-4                                                                               Not calculated                                                             BS-3                                                                           BS-5                                                                           BS-6                                                                           __________________________________________________________________________

                                      TABLE 2                                      __________________________________________________________________________     Composition  mol %        Solubility (ppm)                                     Comp.                                                                              CaO                                                                               MgO                                                                               SrO                                                                               ZrO2                                                                              Al2O3                                                                              TiO2                                                                              SiO2                                                                              CaO                                                                               MgO/SrO                                                                             SiO2                                                                              Total                                     __________________________________________________________________________     CaO--SrO--ZrO2--SiO2 System                                                    F33 30.2                                                                              0.9                                                                               2.6                                                                               5  0.2 0.1                                                                               60.9                                                                              22 12   29 63.00                                     F28 31.6                                                                              0.9                                                                               2.6                                                                               2.4                                                                               0.3 0.1                                                                               62.1                                                                              43 16   78 137.00                                    F15 27.7                                                                              0.9                                                                               2.8                                                                               5  0.1 0.1                                                                               63.4                                                                              17 11   22 50.00                                     F34 24.9                                                                              0.8                                                                               5.7                                                                               4.8                                                                               0.2 0.1                                                                               63.6                                                                              19 14   27 60.00                                     F20 25.8                                                                              0.8                                                                               2.7                                                                               5.4                                                                               0.1 0.1                                                                               65.2                                                                              11 10   15 36.00                                     F1  29.4                                                                              0.9                                                                               2.7                                                                               2.5                                                                               0.1 0.1                                                                               64.3                                                                              32 14   60 106.00                                    F29 26.6                                                                              0.8                                                                               5.5                                                                               2.5                                                                               0.2    64.4                                                    F16 22.7                                                                              0.8                                                                               5.7                                                                               5.2                                                                               0.1 0.1                                                                               65.4                                                                              15 12   17 44.00                                     F6  27.3                                                                              0.8                                                                               2.6                                                                               2.5                                                                               0.1 0.1                                                                               66.6                                                                              30 12   53 95.00                                     F2  24.3                                                                              0.6                                                                               5.7                                                                               2.5                                                                               0.1 0.1                                                                               66.7                                                                              24 17   48 89.00                                     F24 23.2                                                                              0.8                                                                               2.7                                                                               5.2                                                                               0.1 0.1                                                                               68 11 10   17 38.00                                     F21 20.2                                                                              0.8                                                                               5.7                                                                               5.4                                                                               0.1 0.1                                                                               67.7                                                                              10 12   14 36.00                                     F11 25.3                                                                              0.8                                                                               2.9                                                                               2.4                                                                               0.1 0.1                                                                               68.4                                                                              20 12   31 63.00                                     F7  22.3                                                                              0.6                                                                               5.6                                                                               2.6                                                                               0.1 0.1                                                                               68.8                                                                              25 19   43 87.00                                     F3  18.8                                                                              0.5                                                                               8.8                                                                               2.7                                                                               0.1 0.1                                                                               69 8  14   32 54.00                                     F25 17.7                                                                              0.7                                                                               5.6                                                                               5.3                                                                               0.1 0.1                                                                               70.6                                                                              13 12   19 44.00                                     F12 19.6                                                                              0.8                                                                               5.6                                                                               2.6                                                                               0.1 0.1                                                                               71.3                                                                              19 17   33 69.00                                     CaO--SrO--SiO2 System                                                          E29 23.3                                                                              0.6                                                                               11.8  0.2    64 33 47   103                                                                               183.00                                    E30 17.8                                                                              0.5                                                                               15.2                                                                              0.1                                                                               0.2 0.1                                                                               66.2                                                                              23 54   92 169.00                                    E19 20 0.6                                                                               12 0.1                                                                               0.3    66.9                                                                              32 52   88 172.00                                    E4  19 0.5                                                                               11.5                                                                              0.2                                                                               0.1 0.1                                                                               68.7                                                                              32 50   69 151.00                                    E20 14.8                                                                              0.7                                                                               15.5                                                                              0.1                                                                               0.3    68.6                                                                              20 53   59 132.00                                    E5  12.9                                                                              0.3                                                                               15.5                                                                              0.1                                                                               0.1 0.1                                                                               71 21 66   54 141.00                                    E26 38.2                                                                              1  2.6   0.2    57.9                                                    E27 33.8                                                                              0.9                                                                               5.6   0.2    59.5                                                                              57 30   148                                                                               235.00                                    E16 36.2                                                                              0.9                                                                               2.6   0.2 0.1                                                                               60 61 13   137                                                                               211.00                                    E28 28.6                                                                              0.9                                                                               8.2   0.2    62 50 44   152                                                                               246.00                                    E17 30.1                                                                              0.8                                                                               5.7   0.3    63.2                                                                              54 27   115                                                                               196.00                                    E6  32 0.9                                                                               2.6   0.2    64.2                                                                              61 16   100                                                                               177.00                                    E1  31.9                                                                              0.8                                                                               2.6   0.2 0.1                                                                               64.4                                                                              71 17   120                                                                               208.00                                    E18 25.3                                                                              0.6                                                                               8.8                                                                               0.1                                                                               0.3    65 39 37   90 166.00                                    E2  27.4                                                                              0.8                                                                               5.4                                                                               0.1                                                                               0.2 0.1                                                                               66 62 32   113                                                                               207.00                                    E7  26.9                                                                              0.6                                                                               5.7   0.2 0.1                                                                               66.5                                                                              54 34   90 178.00                                    E11 29.7                                                                              0.7                                                                               2.6   0.2 0.1                                                                               66.6                                                                              50 12   90 152.00                                    E3  22.4                                                                              0.6                                                                               8.3                                                                               0.1                                                                               0.1 0.1                                                                               68.4                                                                              44 41   84 169.00                                    E12 23.5                                                                              0.6                                                                               5.7                                                                               0.2                                                                               0.4    69.7                                                                              44 31   87 162.00                                    __________________________________________________________________________ 

What is claimed is:
 1. A strontium containing refractory fibre for which a vacuum cast preform of the fiber has a shrinkage of 3.5% or less when exposed to 1260° C. for 24 hours and consisting essentially of CaO, SiO₂, SrO, and optionally ZrO₂, and wherein any incidental impurities comprising MgO, iron oxides, and alkali metal oxides amount to less than 2 mol % in total, and in which excess SiO₂, defined as the amount of SiO₂ calculated as remaining after the above named constituents are crystallized as silicates, exceeds 26 mol %.
 2. The refractory fibre as claimed in claim 1 wherein the amount of CaO is less than 33.8 mol % and the amount of SiO₂ is more than 62.1 mol %.
 3. The refractory fibre as claimed in claim 2 wherein:the amount of CaO is about 12.9 to about 31.9 mol %; the amount of SrO is about 2.6 to about 15.5 mol %; the amount of SiO₂ is about 63.2 to about 71.3 mol %; and the amount of ZrO₂ is 0 to about 5.4 mol %.
 4. The refractory fibre as claimed in claim 1, wherein the amount of MgO is about 1 mol % or less.
 5. The refractory fibre as claimed in claim 1, consisting essentially of CaO, SrO, and SiO₂, wherein the excess SiO₂ remaining after crystallization of CaO as CaSiO₃ and crystallization of SrO as SrSiO₃ exceeds 26 mol %.
 6. The refractory fibre as claimed in claim 5, having a mole ratio of crystallized CaSiO₃ to crystallized SrSiO₃ of greater than about
 2. 7. The refractory fibre as claimed in claim 5, having a mole ratio of crystallized CaSiO₃ to crystallized SrSiO₃ of less than about 0.5.
 8. The refractory fibre as claimed in claim 5, wherein the excess SiO₂ exceeds 34 mol %.
 9. The refractory fibre as claimed in claim 8, having a mole ratio of crystallized CaSiO₃ to crystallized SrSiO₃ of between about 0.5 and about
 2. 10. The refractory fibre as claimed in claim 1 consisting essentially of CaO, SrO, SiO₂, and ZrO₂ wherein the excess SiO₂ remaining after crystallization of ZrO₂ as 6SrO.ZrO₂.5SiO₂ and 2CaO.ZrO₂.4SiO₂, crystallization of CaO as 2CaO.ZrO₂.4SiO₂ and CaSiO₃, and crystallization of SrO as 6SrO.ZrO₂.5SiO₂, is greater than 26 mol %.
 11. A method of providing refractory properties to an article comprising:(a) selecting a strontium containing refractory fibre for which a vacuum cast preform of the fiber has a shrinkage of 3.5% or less when exposed to 1260° C. for 24 hours and consisting essentially of CaO, SiO₂, SrO, and optionally ZrO₂, and wherein any incidental impurities comprising MgO, iron oxides, and alkali metal oxides amount to less than 2 mol % in total and in which excess SiO₂, defined as the amount of SiO₂ calculated as remaining after the above named constituents are crystallized as silicates, exceeds 26 mol %; (b) associating the refractory fibre in or with an article; and (c) subjecting the fibre and article to an elevated temperature of at least 1000° C. 